2250Y 注塑级、增强级
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.20 | --- |
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % | |
| 阻燃性 | 厚度1.47mm(厚度3.05mm ) | UL 94 | 94V-2 | --- | |
| 机械性能 | 折射率 | --- | ASTM D-542 | 1.585 | --- |
| 拉伸强度屈服点断裂点 | -- | ASTM D-638ASTMD-638 | 62(630)78(800) | Mpa(kgf/cm2)Mpa(kgf/cm2) | |
| 拉伸模量 | --- | ASTM D-638 | 2130(21700) | Mpa(kgf/cm2) | |
| 拉伸率屈服点断裂点 | -- | ASTM D-638ASTMD-638 | 6140 | -- | |
| 弯曲强度 | --- | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |
| 弯曲模量 | --- | ASTM D-790 | 2260(23000) | Mpa(kgf/cm2) | |
| 压缩强度 | --- | ASTM D-695 | 76(780) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 830(85) | j/m(kgf.cm/cm) | |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 130(13) | j/m(kgf.cm/cm) | |
| 洛氏硬度 | --- | ASTM D-785 | 77 | M标度 | |
| 电气性能 | 耐导电径迹性（CTI） | --- | IEC 112 | 300 | V |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | |
| 体积电阻率 | --- | ASTM D-257 | 3 | 1016Ω.cm | |
| 介电率 | 60Hz(106Hz) | ASTM D-150 | 2.95(2.9) | --- | |
| 介电正切 | 60Hz(106Hz) | ASTM D-150 | 0.0004(0.009) | --- | |
| 耐电弧性 | --- | ASTM D-495 | 110 | sec | |
| 加工性能 | 成型收缩率流动方向垂直方向 | -- | ASTM D-955ASTMD-955 | 0.5～0.70.5～0.7 | %% |
| 热 性 能 | 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 142 | ℃ |
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 132 | ℃ | |
| 线膨胀系数 | 流动方向(垂直方向) | ASTM D-696 | 7 | 10-5cm/cm/℃ | |
| 温度指数电学式冲击式非冲击式 | 厚度1.47mm厚度1.47mm厚度1.47mm | UL 746BUL 746BUL 746B | |||